Preparation of Bimodal Inorganic Uio-66 Nanocomposite Membrane Via Ex-situ Deposition for Enhanced Nanofiltration
Shangkum Yildun Goji — Department of Chemistry, Faculty of Natural Sciences, University of Jos, P.M.B 2084, Jos, Nigeria *
Saraya Akuben Yakubu — Department of Chemistry, Faculty of Natural Sciences, University of Jos, P.M.B 2084, Jos, Nigeria
Rotbe Gurumji — Plateau State College of Agriculture, Garkawa, P.M.B 001, Mikang, Plateau State, Nigeria
Moses Titus Yilleng — Department of Chemistry, Faculty of Natural Sciences, University of Jos, P.M.B 2084, Jos, Nigeria
Ohwimu Joseph Godday — Department of Chemistry, Federal University of Petroleum Resources, Effurun, Delta State, Nigeria
Muhammad Ibrahim — Department of Chemistry, Faculty of Natural Sciences, University of Jos, P.M.B 2084, Jos, Nigeria
Solomon Almanto Mamuru — Department of Pure and Applied Chemistry, Adamawa State University, Mubi
Saraya Akuben Yakubu — Department of Chemistry, Faculty of Natural Sciences, University of Jos, P.M.B 2084, Jos, Nigeria
Rotbe Gurumji — Plateau State College of Agriculture, Garkawa, P.M.B 001, Mikang, Plateau State, Nigeria
Moses Titus Yilleng — Department of Chemistry, Faculty of Natural Sciences, University of Jos, P.M.B 2084, Jos, Nigeria
Ohwimu Joseph Godday — Department of Chemistry, Federal University of Petroleum Resources, Effurun, Delta State, Nigeria
Muhammad Ibrahim — Department of Chemistry, Faculty of Natural Sciences, University of Jos, P.M.B 2084, Jos, Nigeria
Solomon Almanto Mamuru — Department of Pure and Applied Chemistry, Adamawa State University, Mubi
Volume: 13, Issue 1
Year: 2025
Pages: 35-48
Published: December 3, 2025
Download PDF
3 views
1 downloads
Abstract
Achieving a balance between flux and rejection remains a key challenge in nanofiltration membrane design for water treatment. In this study, a bimodal inorganic UiO-66 nanocomposite membrane was fabricated using an ex-situ deposition method and evaluated for filtering organic contaminants from water. Polydispersed UiO-66 nanoparticles (14 and 108 nm) were synthesized by modulating water content (0.2–2.0 mL) during synthesis. Characterization via XRD, TEM, FTIR, and TGA confirmed the structure and distribution of UiO-66. XRD results showed characteristic peaks at 2θ = 7.34° and 8.48°, indicating the formation of a face-centered cubic crystal structure. Peak broadening at 2θ = 8.6° and 10° was observed with increased water addition. TEM analysis revealed the impact of water modulation on nanoparticle size. Unimodal UiO-66 suspensions (14 and 108 nm) were deposited on a microfiltration regenerated cellulose (RC) support via suction filtration (900 mbar, 30 min), forming a bimodal membrane. After partial drying, the membranes were tested for methylene blue rejection. At 99% rejection and 900 mbar pressure, the bimodal UiO-66 membrane achieved a high water permeability of 400 ± 5.33 L/m²/h. These results demonstrate the potential of ex-situ synthesized bimodal UiO-66 membranes for efficient nanofiltration in water treatment.